Epoxy Fiberglass Sheet Fr4 Sheet G10 unclad laminate Sheet with Good Mechanical and Electrical Insulating Property
Product Description
This product was laminated by the high temperature and high pressure with electronic glassfiber cloth impregnated with brominated epoxy resin.It with high mechanical properties,dielectric properties and flame retardant properties,it also with good heat resistance and moisture resistance;
FR-4 is a code of a grade of flame-resistant materials, which means a material specification that a resin material must be able to extinguish by itself after burning. It is not a material name, but a material grade. The name FR4 comes from the NEMA grading system where the ‘FR’ stands for ‘fire retardant’, compliant with the UL94V-0 standard. Therefore, general PCB circuit boards, There are many types of FR-4 grade materials used, but most of them are composite materials made of Tera-Function epoxy resin with filler and glass fiber.
Compliance With Standards
In accordance with GB/T 1303.4-2009 electrical thermosetting resin industrial hard laminates - Part 4: epoxy resin hard laminates, IEC 60893-3-2-2011 insulating materials - electrical thermosetting resin industrial hard laminates - Part 3-2 of the individual material specification EPGC202.
Features
1.High mechanical properties;
2.High dielectric properties;
3.Good Mechinability
4.Good moisture resistance;
5.Good heat resistance;
6.Temperature resistance:Grade B
7.Flame retardant property:UL94 V-0
Application
This product is mainly used as the structure parts for Motor and electrical equipment,including all kinds of switch、electric equipment、FPC reinforcement plate、carbon film printed circuit boards、computer drilling pad、mould and smelting equipment(PCB test flame）;and also suitable under wet environment and transformer oil.
Main Performance Index
| NO. | ITEM | UNIT | INDEX VALUE | ||
| 1 | Density | g/cm³ | 1.8-2.0 | ||
| 2 | Water absorption Rate | % | ≤0.5 | ||
| 3 | Vertical bending strength | MPa | ≥340 | ||
| 4 | Vertical compression strength | MPa | ≥350 | ||
| 5 | Parallel impact strength (charpy type-gap) | KJ/m² | ≥37 | ||
| 6 | Parallel shear strength | Mpa | ≥34 | ||
| 7 | Tensile strength | MPa | ≥300 | ||
| 8 | Vertical electric strength （in oil of 90℃±2℃） |
1mm | KV/mm | ≥14.2 | |
| 2mm | ≥11.8 | ||||
| 3mm | ≥10.2 | ||||
| 9 | Parallel breakdown voltage(in oil of 90℃±2℃） | KV | ≥40 | ||
| 10 | Dielectric dissiption factor（50Hz) | - | ≤0.04 | ||
| 11 | Insulation Resistance | Normal | Ω | ≥5.0×1012 | |
| After soaking for 24hours | ≥5.0×1010 | ||||
| 12 | Combustibility（UL-94) | Level | V-0 | ||