Product Description
This product is a laminated sheet which is made of eletrical alkali free glass cloth impregnated with melamine resine by hot pressing.
Features
1.Good arc resistance properties;
2.Good dielectric properties ;
3.High Mechanical strength
4.Flame resistance:UL 94 V-0
Main Performance Index
| NO. | ITEM | UNIT | INDEX VALUE | ||
| 01 | Density | g/cm³ | 1.8-2.0 | ||
| 02 | Water absorption | % | ≤2 | ||
| 03 | Vertical bending strength | MPa | ≥200 | ||
| 05 | Parallel impact strength（Charpy type） | KJ/m² | ≥25 | ||
| 07 | Vertical electric strength（in oil of 90℃±2℃） | 1mm | MV/m | ≥7.0 | |
| 2mm | |||||
| ≥5.4 | |||||
| 3mm | |||||
| ≥5.0 | |||||
| 08 | Parallel breakdown voltage（in oil of 90℃±2℃） | KV | ≥15 | ||
| 09 | Comparative creepage tracking index | - | ≥500 | ||
| 10 | Arc resistance | S | 180 | ||
| 11 | Insulation resistance | Normal | Ω | ≥5.0×1010 | |
| After soaking for 24 hours | |||||
| ≥5.0×10 | |||||
| Fire resistance | - | FV0 | |||
Product detail pictures:
Related Product Guide:
go on to boost, to be certain item quality in line with market and buyer standard demands. Our firm has a excellent assurance procedure happen to be established for PriceList for Fiberglass Products - 3233 Melamine Glassfiber Lamiated Sheet – Xinxing, The product will supply to all over the world, such as: Netherlands, Turkey, Slovakia, Our factory is equipped with complete facility in 10000 square meters, which makes us be able to satisfy the producing and sales for most auto part solutions. Our advantage is full category, high quality and competitive price! Based on that, our products win a high admiration both at home and abroad.
By King from Casablanca - 2017.08.18 11:04
The goods are very perfect and the company sales manager is warmful, we will come to this company to purchase next time.
By Mandy from Rotterdam - 2018.06.28 19:27